Diamond inlaid composite plating

Tools (such as drills, reamers, abrasive, roller, etc.) of diamond, cubic boron nitride and other superhard materials have been prepared to produce oil, and coal industry exploration and machinery, instruments, electronics and other minerals in the A large number of applications have been obtained in equipment processing. Preparing diamond tools are mainly two kinds of powder metallurgy and composite plating. Compared with the powder metallurgy method, the composite plating method has a simple equipment, can reduce the loss of the mold, does not cause the diamond to be subjected to heat loss, and is easy to repair, and thus has a place in the manufacture of the diamond tool. Depending on the number of layers of diamond particles embedded in the surface of the diamond tool, the manufacturing method can be divided into two types: the table setting method and the gestation method.
The process of the impregnation method is generally as follows: pretreatment - plating of diamond-free matrix metal Ni or Ni-Co) - sand plating - re-plating 3 ~ 5 μm bright nickel - surface finishing.
The specification of electroplated nickel-based diamond inlay plating is as follows: nickel sulfate 220-240g/L, cobalt sulfate 15-30g/L, boric acid 25-35g/L, sodium chloride 10-20g/L, 1,4-butyne II Alcohol 0.6-0.8 g/L, saccharin 0.8-1.0 g/L, sodium lauryl sulfate 0.08-0.1 g/L, diamond (5-7 μm) 5-10 g/L, temperature 45-50 ° C, pH 4.1 to 4.5, current density 2A/dm 2 , strong agitation of air.

Wax And Candle

Wax And Candle,Soy Wax Flakes,Coconut Wax,Jelly Wax

Tianjin Centerstar Chemical Co., LTD. , https://www.centerstarchem.com